Industrial Raw Materials

Specifications:

Grade: Various grades such as Bituminous, Sub-Bituminous, and Anthracite coal.

Moisture content: 10-40%

Ash content: 5-30%

Volatile matter: 20-40%

Calorific value: 4,500-6,000 kcal/kg

Sulfur content: 0.5-3.0%

Size: Lump or pulverized coal

Specifications:

Grade: Various grades such as Raw Petcoke, Calcined Petcoke, and Spherical Petcoke.

Moisture content: 5-15%

Ash content: 10-30%

Volatile matter: 10-20%

Fixed carbon content: 60-90%

Size: Lump or pulverized coke

Specifications:

Composition: Propane (50-70%), Butane (30-50%), Ethane (<10%)

Purity: 95% or higher

Density: 1.2-1.4 g/cm3 o Vapor pressure: 1.2-1.8 bar (gauge)

Specifications:

EN590: Complies with European Standard EN 590:2013

Sulfur content: ≤10 ppm (parts per million)

Cetane number: ≥51

Density at 15°C: 0.820-0.845 g/cm3

Flash point: ≥55°C

Pour point: ≤ -20°C

Specifications:

EN590: Complies with European Standard EN 590:2013

Sulfur content: ≤50 ppm (parts per million)

Cetane number: ≥51

Density at 15°C: 0.820-0.845 g/cm3

Flash point: ≥55°C

Pour point: ≤ -20°C

Specifications:

NATO F-34 or ASTM D1655: Complies with relevant international standards

Sulfur content: ≤1,000 ppm (parts per million)

Cetane number: ≥40

Density at 15°C: 0.820-0.845 g/cm3

Flash point: ≥38°C

Pour point: ≤ -40°C

Specifications:

RON (Research Octane Number): ≥95

MON (Motor Octane Number): ≥85

Sulfur content: ≤100 ppm (parts per million)

Density at 15°C: 0.720-0.740 g/cm3

Flash point: ≥38°C

Pour point: ≤ -30°C

Specifications:

-RON (Research Octane Number): ≥95

MON (Motor Octane Number): ≥85

Sulfur content: ≤150 ppm (parts per million)

Density at 15°C: 0.720-0.740 g/cm3

Flash point: ≥38°C

Pour point: ≤ -30°C

Specifications:

-API gravity: 16-20° API

Viscosity at 50°C: 150-300 cSt

Sulfur content: ≤3.5%

Ash content: ≤1%

Water content: ≤1%

Specifications:

Vary depending on the specific crude oil:

API gravity (°API): Varies (e.g., 30°API, 40°API, etc.)

Viscosity at 50°C (cSt): Varies (e.g., 1.5 cSt, 2.5 cSt, etc.)

Sulfur content (%): Varies (e.g., 0.5%, 1%, etc.)

Ash content (%): Varies (e.g., 0.1%, 0.5%, etc.)

Water content (%): Varies (e.g., 0.1%, 1%, etc.)

Specifications:

Grade: Various grades such as Hematite, Magnetite, and Limonite.

Iron content: 50-70%

Silica content: 5-15%

Alumina content: 1-5%

Size: Lump or fines

Specifications:

Vary depending on the specific grade:

HMS 1:

Iron content: 90% or higher

Contaminants: Low levels of copper, zinc, and other metals

HMS 2:

Iron content: 80% or higher

Contaminants: Higher levels of copper, zinc, and other metals

Specifications:

Vary depending on the specific alloy:

Al99.7% min

Silicon content: <0.2% o Copper content: <0.2% Magnesium content: <0.05%

Specifications:

Vary depending on the specific alloy:

Al99.7% min

Silicon content: <0.2% o Copper content: <0.2% o Magnesium content: <0.05%

Specifications:

Vary depending on the specific grade:

Copper content: 99.9% min

Impurities: Oxygen (O): <100 ppm Sulfur (S): <50 ppm Gold (Au): <0.01 ppm Silver (Ag): <0.01 ppm

Specifications:

Vary depending on the specific alloy:

Copper content: Varying amounts (e.g., Cu60-Zn40)

Purity level: Depending on the application

Specifications:

Vary depending on the specific grade:

OPC 42.5: Blast furnace slag cement with a compressive strength of at least 42.5 MPa Calcium oxide (CaO) content: >65% Silica (SiO2) content: >15% Aloxide (Al2O3) content: >4% Lime saturation factor (LSF): ≥0.45 OPPC clinker strength (OPPC): ≥42.5 MPa OPPA clinker strength (OPPA): ≥42.5 MPa

OPC 52.5: Blast furnace slag cement with a compressive strength of at least 52.5 MPa Calcium oxide (CaO) content: >65% Silica (SiO2) content: >15% Alox